KEEMILISED OMADUSED
| CU | SI | FE | MN | MG | ZN |
|---|---|---|---|---|---|
| 0,25 protsenti | 0,30 protsenti | 0,70 protsenti max | 1-1,50 protsenti | 0.80-1.30 protsenti | 0,25 protsenti |
MEHAANILISED OMADUSED
| HINNE | TUGUS (METRIC/IMPERIAAL) | PIKENEMINE | KAREDUS | |||
|---|---|---|---|---|---|---|
| Karastus | Ülim tõmbetugevus | Ülim tootlikkuse tugevus | Nihketugevus | Väsimus Tugevus | protsenti | Brinell |
| 3004-O | 180 MPa / 26,000 psi | 69 MPa / 10, 000 psi | 110 MPa / 16,000 psi | 97 MPa / 14,000 psi | 20-25 | 45 |
| 3004-H34 | 215 MPa / 31, 000 psi | 170 MPa / 25, 000 psi | 115 MPa / 17,000 psi | 105 MPa / 15,000 psi | 10-17 | 52 |
| 3004-H36 | 240 MPa / 35, 000 psi | 200 MPa / 25, 000 psi | 125 MPa / 18,000 psi | 105 MPa / 15,000psi | 9-12 | 63 |
| 3004-H36 | 260 MPa / 38, 000 psi | 230 MPa / 33, 000 psi | 140 MPa / 20, 000 psi | 110 MPa / 16,000 psi | 5-9 | 70 |
| 3004-H38 | 285 MPa / 41, 000 psi | 250 MPa / 36, 000 psi | 145 MPa / 21,000 psi | 110 MPa / 16,000 psi | 4-6 | 77 |
KORDUMA KIPPUVAD KÜSIMUSED
MIS ERINEB 3003 JA 3004 ALUMIINIUM?KAS 3004 ALUMIINIUM KASUTATAKSE KÖÖGITÕISTEKS?MIS ON 3004 KASUTUSED?
Mis vahe on 3003 ja 3004 alumiiniumil?
VASTUS:
Need kaks üldotstarbelist sulamit on väga sarnased. Keemilise koostise poolest on alumiiniumil 3004 lisatud magneesiumi, mis annab sellele klassile tugevuse osas ülekaalu.